ASTM A240 Grade 304LN Heat-Treated refers to a specific heat-treated variant of stainless steel grade 304LN as per the ASTM A240 standard.
Grade 304LN is an austenitic stainless steel with low carbon content, which offers excellent corrosion resistance and good mechanical properties. The "LN" in the grade designation stands for "low nitrogen," indicating reduced nitrogen content compared to standard grade 304.
The heat treatment process applied to ASTM A240 Grade 304LN involves subjecting the material to controlled heating and cooling conditions to modify its microstructure and enhance certain properties. Heat treatment can improve the material's strength, hardness, and other mechanical characteristics based on specific requirements.
|
Property
|
Temperature
|
Value
|
Comment
|
|---|---|---|---|
|
Density
|
23.0 °C
|
7.9 - 8.2 g/cm³
Show Material materials with Density of 7.9 - 8.2 g/cm³
|
Typical for Austenitic Stainless Steel
|
|
Property
|
Temperature
|
Value
|
Comment
|
|---|---|---|---|
|
Elastic modulus
|
23.0 °C
|
195 GPa
Show Material materials with Elastic modulus of 195 GPa
|
Typical for Austenitic Stainless Steel
|
|
Elongation A50
|
23.0 °C
|
40 %
Show Material materials with Elongation A50 of 40 %
|
|
|
Hardness, Brinell
|
23.0 °C
|
217 [-]
Show Material materials with Hardness, Brinell of 217 [-]
|
|
|
Hardness, Rockwell B
|
23.0 °C
|
95 [-]
Show Material materials with Hardness, Rockwell B of 95 [-]
|
|
|
Poisson's ratio
|
23.0 °C
|
0.3 [-]
Show Material materials with Poisson's ratio of 0.3 [-]
|
Typical for Austenitic Stainless Steel
|
|
Shear modulus
|
23.0 °C
|
77 GPa
Show Material materials with Shear modulus of 77 GPa
|
Typical for Austenitic Stainless Steel
|
|
Tensile strength
|
23.0 °C
|
515 MPa
Show Material materials with Tensile strength of 515 MPa
|
|
|
Yield strength Rp0.2
|
23.0 °C
|
205 MPa
Show Material materials with Yield strength Rp0.2 of 205 MPa
|
|
|
Yield strength Rp1.0
|
23.0 °C
|
310 MPa
Show Material materials with Yield strength Rp1.0 of 310 MPa
|
|
|
Property
|
Temperature
|
Value
|
Comment
|
|---|---|---|---|
|
Coefficient of thermal expansion
|
23.0 °C
|
1.7E-5 - 1.9E-5 1/K
Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K
|
Typical for Austenitic Stainless Steel
|
|
Melting point
|
|
1230 - 1480 °C
Show Material materials with Melting point of 1230 - 1480 °C
|
Typical for Austenitic Stainless Steel
|
|
Specific heat capacity
|
23.0 °C
|
440 J/(kg·K)
Show Material materials with Specific heat capacity of 440 J/(kg·K)
|
Typical for Austenitic Stainless Steel
|
|
Thermal conductivity
|
23.0 °C
|
11 - 21 W/(m·K)
Show Material materials with Thermal conductivity of 11 - 21 W/(m·K)
|
Typical for Austenitic Stainless Steel
|
|
Property
|
Temperature
|
Value
|
Comment
|
|---|---|---|---|
|
Electrical resistivity
|
23.0 °C
|
8.5E-7 Ω·m
Show Material materials with Electrical resistivity of 8.5E-7 Ω·m
|
Typical for Austenitic Stainless Steel
|
|
Property
|
Value
|
|---|---|
|
Carbon
|
0.03 %
Show Material materials with Carbon of 0.03 %
|
|
Chromium
|
18 - 20 %
Show Material materials with Chromium of 18 - 20 %
|
|
Manganese
|
2 %
Show Material materials with Manganese of 2 %
|
|
Nickel
|
8 - 12 %
Show Material materials with Nickel of 8 - 12 %
|
|
Nitrogen
|
0.1 - 0.16 %
Show Material materials with Nitrogen of 0.1 - 0.16 %
|
|
Phosphorus
|
0.05 %
Show Material materials with Phosphorus of 0.05 %
|
|
Silicon
|
0.75 %
Show Material materials with Silicon of 0.75 %
|
|
Sulfur
|
0.03 %
Show Material materials with Sulfur of 0.03 %
|
Our steel products are used in world-renowned shipbuilding and machinery industries. Our premium galvanized steel coils are used in construction, automotive manufacturing and other areas where strength and resilience are required.